OK AUTROD 308LSI ESAB WIRE DIAM 0.8 FOR WELDING COMMON STAINLESS STEELS 15 KG REEL
MIG welding of austenitic stainless steels such as AISI 301, 304, 304L and similar.
Type 308L wire for MIG welding of corrosion-resistant stainless steels of nominal analysis 18Cr-8Ni. The low carbon deposit makes it particularly suitable where there is a risk of intergranular corrosion. The high silicon content improves its weldability. The wire is widely used in the manufacture of components for the chemical and food industries.
OK AUTROD 308LSI ESAB WIRE DIAM 0.8 FOR WELDING COMMON STAINLESS STEELS 15 KG REEL
€406.75
VAT included
1612089820
MIG welding of austenitic stainless steels such as AISI 301, 304, 304L and similar.
Type 308L wire for MIG welding of corrosion-resistant stainless steels of nominal analysis 18Cr-8Ni. The low carbon deposit makes it particularly suitable where there is a risk of intergranular corrosion. The high silicon content improves its weldability. The wire is widely used in the manufacture of components for the chemical and food industries.
Security policy
(edit with the Customer Reassurance module)
Delivery policy
(edit with the Customer Reassurance module)
Return policy
(edit with the Customer Reassurance module)
Typical tensile properties
| Stretching | Tensile strength | Abrasion resistance | State | Shielding gas |
| 36 % | 570 MPa | 400 MPa | As Welded | - |
| 25 % | 490 MPa | 370 MPa | As Welded | Tested at 350°C. |
Charpy proof estate with V-inlay
| State | Test temperature | Values tenacity |
| As Welded | 20 °C | 110 J |
| As Welded | -60 °C | 70 J |
| As Welded | -196 °C | 45 J |
Weld metal analysis
| Wire composition | |||||||
| Mn | Now | The | C | Yes | Ferrite FN | Ni | Cr |
| 1.8 % | 0.15 % | 0.10 % | 0.01 % | 0.9 % | 9 % | 10.5 % | 19.9 % |
Filing date
| Diameter | Amp | Deposit Rate | Wire drag speed | High |
| 0.6 mm | - | - | - | - |
| 0.8 mm | 55-160 A | 1.0–4.1 kg/h | 4.0–17.0 m/min | 15-24 V |
| 0.9 mm | 65-220 A | 1.1–5.4 kg/h | 3.5–18.0 m/min | 15-28 V |
| 1.0 mm | 80-240 A | 1.5–6.0 kg/h | 4.0–16.0 m/min | 15-28 V |
| 1.14 mm | - | - | - | - |
| 1.2 mm | 100-300 A | 1.6–7.5 kg/h | 3.0–14.0 m/min | 15-29 V |
| 1.6 mm | 230–375 A | 5.2–8.6 kg/h | 5.5–9.0 m/min | 23-29 V |
| Endorsements: | BV; 308L SA BT (M12); CE; EN 13479; CWB; ER308LSi; DB; 43,039.01; DNV-GL; VL 308 L (M13); NACS/HAKC; 0.8-1.2 mm; VdTUV; 04267 |
| Ranking: | EN ISO 14343-A; G 19 9 L Si; Wire Electrode; SFA/AWS A5.9; ER308LSi; Wire Electrode; Workshop Number; ~1.4316; Wire Electrode |
Approvals are specific to each production site.
| Type of alloy: | Austenitic (with approx. 8 % ferrite) 19% Cr - 9% Ni - Low C - High Si |