OK AUTROD 316LSI ESAB WIRE DIAM 1.0 FOR WELDING 316 STAINLESS STEEL 15 KG REEL
MIG welding of austenitic steels of the AISI 316, 316L type and similar
Corrosion-resistant stainless solid wire for MIG welding of alloy steels such as 18% Cr -8% Ni and 18% Cr -10% Ni -3% Mo. Good resistance to corrosion in general and excellent resistance to corrosion in acidic and chlorinated environments. The low carbon in the deposit recommends its use when there is a risk of intergranular corrosion. Good operational properties of weldability due to the high silicon content.
OK AUTROD 316LSI ESAB WIRE DIAM 1.0 FOR WELDING 316 STAINLESS STEEL 15 KG REEL
€430.08
VAT included
1632109820
MIG welding of austenitic steels of the AISI 316, 316L type and similar
Corrosion-resistant stainless solid wire for MIG welding of alloy steels such as 18% Cr -8% Ni and 18% Cr -10% Ni -3% Mo. Good resistance to corrosion in general and excellent resistance to corrosion in acidic and chlorinated environments. The low carbon in the deposit recommends its use when there is a risk of intergranular corrosion. Good operational properties of weldability due to the high silicon content.
Security policy
(edit with the Customer Reassurance module)
Delivery policy
(edit with the Customer Reassurance module)
Return policy
(edit with the Customer Reassurance module)
Typical tensile properties
| Stretching | Tensile strength | Abrasion resistance | State | Shielding gas |
| 37 % | 560 MPa | 400 MPa | As Welded | - |
| 26 % | 440 MPa | 340 MPa | As Welded | Tested at 350°C. |
Charpy proof estate with V-inlay
| State | Test temperature | Values tenacity |
| As Welded | 20 °C | 120 J |
| As Welded | -60 °C | 95 J |
| As Welded | -110 °C | 70 J |
| As Welded | -196 °C | 45 J |
Weld metal analysis
| Wire composition | |||||||
| Mn | Now | The | C | Yes | Ferrite FN | Ni | Cr |
| 1.8 % | 2.60 % | 0.12 % | 0.01 % | 0.9 % | 7 % | 12.2 % | 18.4 % |
Filing date
| Diameter | Amp | Deposit Rate | Wire drag speed | High |
| 0.6 mm | - | - | - | - |
| 0.8 mm | 55-160 A | 1.0–4.1 kg/h | 4.0–17.0 m/min | 12-24 V |
| 0.9 mm | 65-220 A | 1.1–5.4 kg/h | 3.5–18.0 m/min | 15-28 V |
| 1.0 mm | 80-240 A | 1.5–6.0 kg/h | 4.0–16.0 m/min | 15-28 V |
| 1.14 mm | - | - | - | - |
| 1.2 mm | 100-300 A | 1.6–7.5 kg/h | 3.0–14.0 m/min | 15-29 V |
| 1.6 mm | 230–375 A | 5.2–8.6 kg/h | 5.5–9.0 m/min | 23–31 V |
| Endorsements: | CE; EN 13479; CWB; ER316LSi; DB; 43,039.05; DNV-GL; VL 316 L (M13); VdTUV; 04268; NACS/HAKC; 0.8–1.2 mm |
| Ranking: | EN ISO 14343-A; G 19 12 3 L Yes; Wire Electrode; SFA/AWS A5.9; ER316LSi; Wire Electrode; Workshop Number; ~1.4430; Wire Electrode |
Approvals are specific to each production site.
| Type of alloy: | Austenitic (with approx. 8 % ferrite) 19% Cr - 12% Ni - 3% Mo - Low C - High Si |