OK Autrod 309LSi ESAB WIRE DIAM 0.8 FOR HETEROGENEOUS WELDING AISI 309 15 KG REEL
Mig welding of AISI 309-309L type steels and also for heterogeneous welding of stainless steels with carbon steels.
Stainless steel wire type 23Cr-12Ni for MIG welding of steels with the same chemical composition. When used for the execution of buffer layers on carbon steel base materials or for welding between dissimilar steels, attention must be paid to dilution. Deposit with good corrosion resistance and, thanks to the high silicon content, good operational weldability properties.
OK Autrod 309LSi ESAB WIRE DIAM 0.8 FOR HETEROGENEOUS WELDING AISI 309 15 KG REEL
€421.33
VAT included
1651089820
Mig welding of AISI 309-309L type steels and also for heterogeneous welding of stainless steels with carbon steels.
Stainless steel wire type 23Cr-12Ni for MIG welding of steels with the same chemical composition. When used for the execution of buffer layers on carbon steel base materials or for welding between dissimilar steels, attention must be paid to dilution. Deposit with good corrosion resistance and, thanks to the high silicon content, good operational weldability properties.
Security policy
(edit with the Customer Reassurance module)
Delivery policy
(edit with the Customer Reassurance module)
Return policy
(edit with the Customer Reassurance module)
Stainless steel wire type 23Cr-12Ni for MIG welding of steels with the same chemical composition. When used for the execution of buffer layers on carbon steel base materials or for welding between dissimilar steels, attention must be paid to dilution. Deposit with good corrosion resistance and, thanks to the high silicon content, good operational weldability properties.
Typical tensile properties
| Stretching | Tensile strength | Yield strength | State |
| 41% | 600 MPa | 440 MPa | As Welded |
Charpy V-notch test properties
| State | Test temperature | Tenacity value |
| As Welded | 20 °C | 160 J |
| As Welded | -60 °C | 130 J |
| As Welded | -110 °C | 90 J |
Weld Metal Analysis
| wire composition | ||||||
| Mn | Mo | Who | C | Yes | No | Cr |
| 1.7 % | 0.15 % | 0.12 % | 0.02 % | 0.9 % | 13.5% | 23.4% |
Deposit data
| Amp | Diameter | Deposit rate | Wire drag speed | Volt |
| 55-160 A | 0.8mm | 1.0-4.1 kg/h | 4.0-17.0 m/min | 15-24V |
| 65-220 A | 0.9mm | 1.1-5.4 kg/h | 3.5-18.0 m/min | 15-28 V |
| 80-240 A | 1.0mm | 1.5-6.0 kg/h | 4.0-16.0 m/min | 15-28 V |
| - | 1.14 mm | - | - | - |
| 100-300 A | 1.2 mm | 1.6-7.5 kg/h | 3.0-14.0 m/min | 15-29 V |
| 230-375 A | 1.6mm | 5.2-8.6 kg/h | 5.5-9.0 m/min | 23-31 V |
| Approvals: | THERE IS; EN 13479; CWB; ER309LSi; DB; 43.039.16; NAKS/HAKC; 1.0MM-1.2MM; VdTÜV; 10020 |
| Classifications: | EN ISO 14343-A; G 23 12 L Yes; Wire Electrode; SFA/AWS A5.9; ER309LSi; Wire Electrode; Werkstoffnummer; ~1.4332; Wire Electrode |
Approvals are specific to each production site.
| Alloy Type: | Austenitic (with approx. 8 % ferrite) 24 % Cr - 13 % Ni - Low C |